At the reparation of the welded body elements, three welding categories may be used:
protection gas welding (CO2), electric spot welding and filling materials welding
(autogenous).
At the autogenous welding, it is recommended that flame must be slightly inclined so
that arch can be seen and the flame extremity to be maintained at aprox. 5 mm from the
part to be welded.
1. Spot welding resistive parameters for steel plates with carbon content C < 0,15 %.
Plate thickness (mm) Welding current (KA) Welding time(per) Tightening force (daNm)
0,5
0,8
1,0
1,25
1,5
2,0
2.Welding parameters for the welding in protector gas for carbon steel plates or lowalloyed
steel.
cross linked
plates welding
Plate thickness (mm)
Electrode diameter (mm)
Welding wire speed (m/min)
Welding current (A)
Welding speed (m/min)
Welding voltage (V)
Protection gas flow(l/min)
Electron free length (mm )
GENERAL
WELDING TYPES AND PARAMETERS
6,5
8,0
9,5
10,5
10,0
12,0
NOTE : 1 period = 1/50 part of a second
Horizontal welding position ( fig. 1 )
end to
corner
end welding
welding
( fig.1 )
0-1,5mm
0,6
0,6
0,8 0,8
2,5
1,9 3,2
35
35 55
0,25
0,25 0,35
17
17 18
40 - 9
5
8
10
10
14
16
( fig.2 )
1,0
1,5
1,0 0,8
1,0 0,8
2,4 4,4
3,8 5,7
80 80
120 100
0,33 0,33
0,50 0,45
18
19
19 20
12 - 17
6 - 12
40
130
200
250
295
310
350
0-1,5mm
2,0
1,0
4,4
130
0,45
20