Lincoln Electric AC-225C Specification Sheet page 112

Consumables
Aluminum MIG Wires
Electrode AWS
Name Class
SuperGlaze ®
SuperGlaze ® 1100 ER1100
SuperGlaze ® 4043 ER4043
SuperGlaze ® 4047 ER4047
SuperGlaze ® 5183 ER5183
SuperGlaze 5356 ER5356
®
SuperGlaze ® 5554 ER5554
SuperGlaze ® 5556 ER5556
Package Code Key: AP = Accu-Pak
114
SuperGlaze ® controls the problems usually associated with aluminum wire feeding such as birdnesting, tangling
and burnback, by providing a pristine surface condition and feeding the wire with less force than typical
competitive products.
General
Description
SuperGlaze ® 1100 is highly resistant to chemical corrosion and has good crack resistance.
Suitable for electrical and chemical applications utilizing aluminum base metal with little
or no alloying elements. Like all 1XXX filler alloys, Lincoln's
aluminum MIG wire and requires extra care to ensure good feeding.
SuperGlaze ® 4043 is a great choice for the welding of heat-treatable base alloys and more
specifically the 6XXX series alloys. It has a lower melting point and more fluidity than the
5XXX series filler alloys and is preferred by welders because of its favorable operating
characteristics. ER4043 type wires are also less sensitive to weld cracking with the 6XXX
series base alloys. SuperGlaze ® 4043 is suitable for sustained elevated temperature service,
i.e. above 150°F (65°C).
A lower melting point and higher fluidity are two advantages SuperGlaze
cousin SuperGlaze ® 4043. SuperGlaze ®
excellent operator appeal. It can be used as a substitute for an ER4043 type wire to increase
silicon in the weld metal, minimize hot cracking, and produce higher fillet weld shear strength.
SuperGlaze ® 4047 is suitable for sustained elevated temperature service, i.e. above 150°F
(65°C).
SuperGlaze ® 5183 is designed to weld high magnesium alloys to meet higher tensile strength
requirements. Use on 5083 and 5654 base materials when required tensile strengths are
40,000 psi (276 MPa) or greater. Typical applications are in the marine and cryogenic
industries, and high strength structural aluminum fabrication.
SuperGlaze 5356 is our most popular aluminum MIG wire. It is a great general purpose filler
®
alloy designed for the welding of 5XXX series alloys when 40,000 psi (276 MPa) tensile
strength is not required. 5356 is often chosen for its high shear strength.
SuperGlaze ® 5554 is intended as a matching filler alloy when welding 5554 base alloys. This
alloy is a lower magnesium content alloy and is often used for automotive wheels, over-the-
road trailers, and rail tank cars where the weld filler metal chemistry must closely match the
base material chemistry to maximize corrosion performance.
SuperGlaze ® 5556 weld deposits will provide matching tensile strengths for the 5XXX alloys,
such as 5083 and 5654. Contains increased amounts of magnesium or manganese compared
to SuperGlaze ® 5356.
® Box CT = Cardboard Carton
www.lincolnelectric.com/welding-consumables
® SuperGlaze ® 1100 is the softest
® 4047 has over its
4047 produces very clean weld deposits and possesses
SP = Plastic Spool
Diameter Package Product
inches Weight Lbs. Number
3/64 16SP EDS28407
.030 20CT(1SP) ED030307
.035 20CT(1SP) ED030308
3/64 20CT(1SP) ED030310
.035 16SP ED028395
3/64 16SP ED028397
3/64 20SP ED029234
1/16 20SP ED030281
3/64 16SP EDS28417
1/16 16SP EDS28418
3/64 16SP EDS28437
1/16 16SP EDS28438
3/64 300AP EDO31825
1/16 300AP EDO31938
.035 20CT(1SP) ED030312
3/64 20CT(1SP) ED030314
.035 16SP ED028385
3/64 16SP ED028387
3/64 20SP ED030282
1/16 20SP ED030283
3/64 300AP ED031826
1/16 300AP EDO30985
3/64 16SP ED029573
1/16 16SP EDS29574
3/64 300AP EDO31827
1/16 300AP EDO31939
3/64 16SP EDS29581
1/16 16SP EDS29582
3/64 300AP EDO31828
1/16 300AP EDO31940